Application: | Industrial Magnet |
---|---|
Shape: | Magnetic Separator |
Coating: | Polishing |
Grade: | N35-N52 (M, H, Sh, Uh, Eh, Ah) |
Type: | Permanent |
Usage: | Industrial Usage |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Model No. | Dimensions (mm) | Rods QTY (PCS) | Weight (KGS) |
||||
Dia. A | Dia. E | Dia. B | C | D | |||
IMLF125/25 | 125 | 168 | 32 | 185 | 300 | 5 | 21 |
IMLF125/32 | 125 | 168 | 38 | 185 | 300 | 5 | 22 |
IMLF125/40 | 125 | 168 | 45 | 185 | 300 | 5 | 23 |
IMLF125/50 | 125 | 168 | 57 | 185 | 300 | 5 | 24 |
IMLF125/65 | 125 | 168 | 76 | 185 | 300 | 5 | 25 |
IMLF160/50 | 160 | 219 | 57 | 220 | 360 | 7 | 32.5 |
IMLF160/65 | 160 | 219 | 76 | 220 | 360 | 7 | 34 |
IMLF160/80 | 160 | 219 | 89 | 220 | 360 | 7 | 36 |
IMLF160/100 | 160 | 219 | 108 | 220 | 360 | 7 | 37.5 |
Surface Treatment | Process | Thickness | Color | SST | PCT |
(μm) | (Hours) | (Hours) | |||
Nickel | Ni | 10 ~ 20 | Bright Silver | > 24 ~ 72 | > 24 ~ 72 |
Ni+Cu+Ni | |||||
Black Nickel | Ni+Cu+Ni | 10 ~ 20 | Bright Black | > 48 ~ 96 | > 48 |
Cr3+Zinc | Zn | 5 ~ 8 | Bright Blue | > 16 ~ 48 | --- |
Cr3+Zn | Shining Color | > 36 ~ 72 | |||
Sn | Ni+Cu+Ni+Sn | 10 ~ 25 | Silver | > 36 ~ 72 | > 48 |
Au | Ni+Cu+Ni+Au | 10 ~ 15 | Gold | > 12 | > 48 |
Ag | Ni+Cu+Ni+Ag | 10 ~ 15 | Silver | > 12 | > 48 |
Epoxy | Epoxy | 10 ~ 20 | Black/ Grey | > 96 | --- |
Ni+Cu+Epoxy | 15 ~ 30 | > 120 | --- | ||
Zn+Epoxy | 15 ~ 25 | > 120 | --- | ||
Passivation | --- | 1 ~ 3 | Dark Grey | Temporary Protection | --- |
Phosphate | --- | 1 ~ 3 | Dark Grey | Temporary Protection | --- |
Curie Temperature (°C)
|
310~380
|
Maximum Working Temperature (°C)
|
80~230
|
Electrical Resistivity (µ.cm)
|
110~170
|
Hardness (Hv)
|
560~580
|
Density (g/cm3)
|
7.4~7.8
|
Relative Recoil Permeability (µrec)
|
1.05
|
Saturation Field Strength (kOe/kA/m)
|
(30-40)/(2,400-3,200)
|
Temp. Coefficient of Br (T.C.α (Br)) (%/°C)
|
-0.12 ~ -0.10
|
Temp. Coefficient of Hcj (T.C.β (Hcj)) (%/°C)
|
-0.6
|